Studija o mikrostrukturi i mehaničkim svojstvima laserskog zavarenog spoja od 1,5 mm Ti-6Al-4V legure titana

Ključne riječi:Ti-6Al-4V legura titana/ lasersko zavarivanje / mikrostruktura / mehanička svojstva

Autori: Fu Heguo, Liu Guangxin, Xie Hongzhi, Jiang Wentong, itd.

Shenyang Aircraft Industry Group Co., Ltd

Izvor: zavarivanje i rezanje

Sažetak: eksperiment laserskog zavarivanja plus zavarivanje modifikacije površine od 1,5 mmTi-6Al-4V legura titana was carried out, and the microstructure and static properties of the joint were observed. The results show that due to the influence of different welding thermal cycles, The structure area of laser welding plus surface modification welding joint can be divided into a base metal area, heat affected area, equiaxed crystal area at the bottom of weld, and columnar crystal area at the top of the weld, there is widmanstatten structure in the weld structure, With the increase of the distance from the fusion line, the microstructure of the heat-affected zone increases ' The volume fraction decreased gradually.

Mehanička svojstva spoja pokazuju da su vlačna čvrstoća i čvrstoća na smicanje ekvivalentne osnovnom metalu, a minimalni ugao savijanja je 35 stepeni, što ukazuje da se spoj može primijeniti u inženjerstvu.

Morfologija zavarenog spoja od legure titanijuma Ti-6Al-4V

Mikrostruktura zone zavara

Morfologija mikrostrukture različitih regija u zoni uticaja toplote

Ispitna vrijednost mehaničkih svojstava spoja

Prosječna vrijednost mehaničkih svojstava spoja